Optimizing the Ion Conductivity and Mechanical Stability of Polymer Electrolyte Membranes Designed for Use in Lithium Ion Batteries: Combining Imidazolium-Containing Poly(ionic liquids) and Poly(propylene carbonate).

State-of-the-art Li batteries suffer from serious safety hazards caused by the reactivity of lithium and the flammable nature of liquid electrolytes. This work develops highly efficient solid-state electrolytes consisting of imidazolium-containing polyionic liquids (PILs) and lithium bis(trifluoromethane sulfonyl)imide (LiTFSI). By employing PIL/LiTFSI electrolyte membranes blended with poly(propylene carbonate) (PPC), we addressed the problem of combining ionic conductivity and mechanical properties in one material. It was found that PPC acts as a mechanically reinforcing component that does not reduce but even enhances the ionic conductivity. While pure PILs are liquids, the tricomponent PPC/PIL/LiTFSI blends are rubber-like materials with a Young's modulus in the range of 100 MPa. The high mechanical strength of the material enables fabrication of mechanically robust free-standing membranes. The tricomponent PPC/PIL/LiTFSI membranes have an ionic conductivity of 10-6 S·cm-1 at room temperature, exhibiting conductivity that is two orders of magnitude greater than bicomponent PPC/LiTFSI membranes. At 60 °C, the conductivity of PPC/PIL/LiTFSI membranes increases to 10-5 S·cm-1 and further increases to 10-3 S·cm-1 in the presence of plasticizers. Cyclic voltammetry measurements reveal good electrochemical stability of the tricomponent PIL/PPC/LiTFSI membrane that potentially ranges from 0 to 4.5 V vs. Li/Li+. The mechanically reinforced membranes developed in this work are promising electrolytes for potential applications in solid-state batteries.

Charge-Compensated N-Doped π-Conjugated Polymers: Toward both Thermodynamic Stability of N-Doped States in Water and High Electron Conductivity.

The understanding and applications of electron-conducting π-conjugated polymers with naphtalene diimide (NDI) blocks show remarkable progress in recent years. Such polymers demonstrate a facilitated n-doping due to the strong electron deficiency of the main polymer chain and the presence of the positively charged side groups stabilizing a negative charge of the n-doped backbone. Here, the n-type conducting NDI polymer with enhanced stability of its n-doped states for prospective "in-water" applications is developed. A combined experimental-theoretical approach is used to identify critical features and parameters that control the doping and electron transport process. The facilitated polymer reduction ability and the thermodynamic stability in water are confirmed by electrochemical measurements and doping studies. This material also demonstrates a high conductivity of 10-2  S cm-1  under ambient conditions and 10-1  S cm-1  in vacuum. The modeling explains the stabilizing effects  for various dopants. The simulations show a significant doping-induced "collapse" of the positively charged side chains on the core bearing a partial negative charge. This explains a decrease in the lamellar spacing observed in experiments. This study fundamentally enables a novel pathway for achieving both thermodynamic stability of the n-doped states in water and the high electron conductivity of polymers.

Charge Carrier Mobility Improvement in Diketopyrrolopyrrole Block-Copolymers by Shear Coating.

Shear coating is a promising deposition method for upscaling device fabrication and enabling high throughput, and is furthermore suitable for translating to roll-to-roll processing. Although common polymer semiconductors (PSCs) are solution processible, they are still prone to mechanical failure upon stretching, limiting applications in e.g., electronic skin and health monitoring. Progress made towards mechanically compliant PSCs, e.g., the incorporation of soft segments into the polymer backbone, could not only allow such applications, but also benefit advanced fabrication methods, like roll-to-roll printing on flexible substrates, to produce the targeted devices. Tri-block copolymers (TBCs), consisting of an inner rigid semiconducting poly-diketo-pyrrolopyrrole-thienothiophene (PDPP-TT) block flanked by two soft elastomeric poly(dimethylsiloxane) (PDMS) chains, maintain good charge transport properties, while being mechanically soft and flexible. Potentially aiming at the fabrication of TBC-based wearable electronics by means of cost-efficient and scalable deposition methods (e.g., blade-coating), a tolerance of the electrical performance of the TBCs to the shear speed was investigated. Herein, we demonstrate that such TBCs can be deposited at high shear speeds (film formation up to a speed of 10 mm s-1). While such high speeds result in increased film thickness, no degradation of the electrical performance was observed, as was frequently reported for polymer-based OFETs. Instead, high shear speeds even led to a small improvement in the electrical performance: mobility increased from 0.06 cm2 V-1 s-1 at 0.5 mm s-1 to 0.16 cm2 V-1 s-1 at 7 mm s-1 for the TBC with 24 wt% PDMS, and for the TBC containing 37 wt% PDMS from 0.05 cm2 V-1 s-1 at 0.5 mm s-1 to 0.13 cm2 V-1 s-1 at 7 mm s-1. Interestingly, the improvement of mobility is not accompanied by any significant changes in morphology.

AB- Versus AA+BB-Suzuki Polycondensation: A Palladium/Tris(tert-butyl)phosphine Catalyst Can Outperform Conventional Catalysts.

A Pd/Pt-Bu3 catalyst having bulky, electron-rich ligands significantly outperforms conventional "step-growth catalysts" Pd(PPh3 )4 and Pd(Po-Tol3 )3 in the Suzuki polycondensation of the AB-type arylene-based monomers, such as some of the substituted fluorenes, carbazoles, and phenylenes. In the AA+BB polycondensation, Pd/Pt-Bu3 also performs better under homogeneous reaction conditions, in combination with the organic base Et4 NOH. The superior performance of Pd/Pt-Bu3 is discussed in terms of its higher reactivity in the oxidative addition step and inherent advantages of the intramolecular catalyst transfer, which is a key step joining catalytic cycles of the AB-polycondensation. These findings are applied to the synthesis of a carbazole-based copolymer designed for the use as a hole conductor in solution-processed organic light-emitting diodes.

Layer-by-Layer Assembly Enabled by the Anionic p-Dopant CN6-CP•-K+: a Route to Achieve Interfacial Doping of Organic Semiconductors.

Highly efficient 2D (interfacial) doping of organic semiconductors, poly(3-hexylthiophene) (P3HT) and TIPS-pentacene, was achieved by a polyelectrolyte-supported layer-by-layer assembly of the dual-mode functional dopant CN6-CP•-K+, having an anionic group for its fixation onto oppositely charged surfaces/molecules as well as electron-deficient groups providing its p-doping ability. Polyelectrolyte-supported dopant layers were used to generate conductive channels at the bottom or at the top of semiconducting films. Unlike to the case of sequentially processed P3HT films doped by F4TCNQ ( Moulé , J. Chem. Mater. 2015 , 27 , 5765 ; Koech , P. K. J. Mater. Chem. C 2013 , 1 , 1876 ; Schwartz , B. J. J. Phys. Chem. Lett. 2015 , 6 , 4786 ), the use of more polar CN6-CP•-K+ dopant and ultrathin polycation separation interlayer enables predominantly interfacial kind of doping placement with no or minimal intercalation of the dopant into the semiconductor bulk. The layered structure of the doped film was proved by transmission electron microscopy of the cross-section and it agrees well with other data obtained in this work. The interfacial doping enabled an impressive conductivity of 13 S/cm even for ultrathin P3HT films. We propose to explain the superior efficiency of the interfacial doping compared to the bulk doping in terms of unperturbed morphology of the semiconductor and high mobility of charge carriers, which are spatially separated from the dopant phase.